  2. Half -temperature hard -curing wrapping resin technique 4000 / techNovit® 4000 (Musashino Denshi, INC.)
Half -temperature hard -curing wrapping resin technique 4000 / techNovit® 4000-TechNovit® 4000 (powder)
Half -temperature hard -curing wrapping resin technique 4000 / techNovit® 4000-Technovit® 4004 (powder)
Half -temperature hard -curing wrapping resin technique 4000 / techNovit® 4000-TechNovit® 4006 (powder)
Half -temperature hard -curing wrapping resin technique 4000 / techNovit® 4000-Technovit® 4071 (powder)
Half -temperature hard -curing wrapping resin technique 4000 / techNovit® 4000-TechNovit® 5000 (powder)
Half -temperature hard -curing wrapping resin technique 4000 / techNovit® 4000-Musashino Denshi, INC.

Half -temperature hard -curing wrapping resin technique 4000 / techNovit® 4000
Musashino Denshi, INC.

Musashino Denshi, INC.'s Response Status

Response Rate

100.0%

Response Time

4.6hours

Company Review

5.0

Very Fast Response

About This Product

■ Features

The TechNovit® series is a kulzer -hardened resin made by Kulzer. Ideal for metal tissue observation, analysis and polishing with optical microscope and electron microscope. The adhesion is high and the shrinkage rate is extremely small, which is extremely small, so it prevents polishing. When you want to avoid the effects of high temperatures and pressure, when you want to quickly embed a sample, or when the embedded resin is hard and requires wear resistance, you can also use it to embed a strict condition. We have a variety of lineups, so you can use it according to all uses. * Molds are also available in various materials. * There are other model numbers

  • Product

    Half -temperature hard -curing wrapping resin technique 4000 / techNovit® 4000

Share this product


1010+ people viewing

Last viewed: 2 minutes ago

Free
Get started with our free quotation service - no cost, no obligation.

No Phone Required
We respect your privacy. You can receive quotes without sharing your phone number.

10 Models of Half -temperature hard -curing wrapping resin technique 4000 / techNovit® 4000

Click on the part number for more information about each product

Image Part Number Price (excluding tax) color mixing ratio 25mm 30mm 40mm 50mm Precautions when mixed Working hours Casting time (22 ° C) Hardening highest temperature Steel ball pushing hardness (N/mm²) DIN53456 Density (g/cm³) Din53479 Shock strength (KJ/m²) Din13907 Bending strength (n/mm²) Water absorption rate (vol.%) DIN53495 Line contraction rate (%) Volume shrinkage rate (%) Solubility storage temperature Preservation period Refractive index
Half -temperature hard -curing wrapping resin technique 4000 / techNovit® 4000-Part Number-TechNovit® 4000 (powder)

TechNovit® 4000 (powder)

Available upon quote

White opaque

0.4

6.5g

9.3G

16.2g

24.4G

Mix the solution I (syrup i) and the solution II (syrup II) first

4 minutes

18 minutes to 24 minutes

122 ℃

103

1.57

1.5

50

2.7

2.7

6.2

Dissolve

25 ° C

Three years

-
Half -temperature hard -curing wrapping resin technique 4000 / techNovit® 4000-Part Number-Technovit® 4000 (solution I)

Technovit® 4000 (solution I)

Available upon quote

White opaque

0.4

6.5g

9.3G

16.2g

24.4G

Mix the solution I (syrup i) and the solution II (syrup II) first

4 minutes

18 minutes to 24 minutes

122 ℃

103

1.57

1.5

50

2.7

2.7

6.2

Dissolve

25 ° C

Three years

-
Half -temperature hard -curing wrapping resin technique 4000 / techNovit® 4000-Part Number-Technovit® 4000 (solution II)

Technovit® 4000 (solution II)

Available upon quote

White opaque

0.2

3.3g

4.7G

8.1g

12.2g

Mix the solution I (syrup i) and the solution II (syrup II) first

4 minutes

18 minutes to 24 minutes

122 ℃

103

1.57

1.5

50

2.7

2.7

6.2

Dissolve

25 ° C

Three years

-
Half -temperature hard -curing wrapping resin technique 4000 / techNovit® 4000-Part Number-Technovit® 4004 (powder)

Technovit® 4004 (powder)

Available upon quote

Transparent

0.63

8.0g

11.0g

20.1g

30.1g

The boiling point is low and the bubbles occur during hardening
By using a pressure vessel techno mat
It is possible to embed while keeping high transparency

2 minutes to 3 minutes

9 minutes to 12 minutes

110 ° C

137

1.14

6.4

95

0.38

2.25/2.08/1.80

1: 1 = 6.75/ 1.8: 1 = 5.8/ 2.3: 1 = 5.4

Swell

25 ° C

Three years

Monomer = 1.420/ polymer = 1.438

Half -temperature hard -curing wrapping resin technique 4000 / techNovit® 4000-Part Number-Technovit® 4004 (solution)

Technovit® 4004 (solution)

Available upon quote

Transparent

0.38

4.7G

6.8g

12.3g

18.1G

The boiling point is low and the bubbles occur during hardening
By using a pressure vessel techno mat
It is possible to embed while keeping high transparency

2 minutes to 3 minutes

9 minutes to 12 minutes

110 ° C

137

1.14

6.4

95

0.38

2.25/2.08/1.80

1: 1 = 6.75/ 1.8: 1 = 5.8/ 2.3: 1 = 5.4

Swell

25 ° C

Three years

Monomer = 1.420/ polymer = 1.438

Half -temperature hard -curing wrapping resin technique 4000 / techNovit® 4000-Part Number-TechNovit® 4006 (powder)

TechNovit® 4006 (powder)

Available upon quote

High transparency

0.63

8.1g

11.2g

20.4g

30.3G

By using a pressure container techno mat, it is possible to embed with high transparency.

4 minutes

9 minutes to 13 minutes

99 ℃

155

1.14

5.8

105

0.3

2.25/2.08/1.80

1: 1 = 6.75/ 1.8: 1 = 5.8/ 2.3: 1 = 5.4

Swell

25 ° C

Three years

Monomer = 1.422

Half -temperature hard -curing wrapping resin technique 4000 / techNovit® 4000-Part Number-Technovit® 4006 (solution)

Technovit® 4006 (solution)

Available upon quote

High transparency

0.38

4.7G

6.8g

12.3g

18.1G

By using a pressure container techno mat, it is possible to embed with high transparency.

4 minutes

9 minutes to 13 minutes

99 ℃

155

1.14

5.8

105

0.3

2.25/2.08/1.80

1: 1 = 6.75/ 1.8: 1 = 5.8/ 2.3: 1 = 5.4

Swell

25 ° C

Three years

Monomer = 1.422

Half -temperature hard -curing wrapping resin technique 4000 / techNovit® 4000-Part Number-Technovit® 4071 (powder)

Technovit® 4071 (powder)

Available upon quote

Green translucent

0.63

8.0g

11.0g

20.1g

30.1g

-

1 minute to 2 minutes

5 minutes to 7 minutes

108 ° C

144

1.19

6.1

94

0.47

1.93

5.8

Swell

25 ° C

Three years

Monomer = 1.439

Half -temperature hard -curing wrapping resin technique 4000 / techNovit® 4000-Part Number-Technovit® 4071 (solution)

Technovit® 4071 (solution)

Available upon quote

Green translucent

0.38

4.7G

6.8g

12.3g

18.1G

-

1 minute to 2 minutes

5 minutes to 7 minutes

108 ° C

144

1.19

6.1

94

0.47

1.93

5.8

Swell

25 ° C

Three years

Monomer = 1.439

Half -temperature hard -curing wrapping resin technique 4000 / techNovit® 4000-Part Number-TechNovit® 5000 (powder)

TechNovit® 5000 (powder)

Available upon quote

brown

0.63

- - - -

It has viscous for 1 minute after mixing
By tapping the mold lightly while viscous, the bubbles generated inside the resin can be removed.

1 minute

7 minutes to 12 minutes

125 ℃

-

2.85

5.0N/mm²

85

2

2.3

7.1

Swell

25 ° C

Three years

Monomer = 1.458/ polymer = 1.434

Click on the part number for more information about each product

Other products of Musashino Denshi, INC.

Reviews shown here are reviews of companies.

Diamon drapping method precision polishing system precision polishing device-Musashino Denshi, INC.

Diamon drapping method precision polishing system precision polishing device

Musashino Denshi, INC.

5.0

1060+ people viewing

Last viewed: 5 hours ago

Response time: 4.65 hours

Lapping Machinery

15 models listed

Diamon drapping method precision polishing system dedicated device-Musashino Denshi, INC.

Diamon drapping method precision polishing system dedicated device

Musashino Denshi, INC.

5.0

260+ people viewing

Last viewed: 5 hours ago

Response time: 4.65 hours

Lapping Machinery
Precision and polishing system sample retention unit standard sample retention attachment attachment-Musashino Denshi, INC.

Precision and polishing system sample retention unit standard sample retention attachment attachment

Musashino Denshi, INC.

5.0

320+ people viewing

Last viewed: 5 hours ago

Response time: 4.65 hours

3 models listed

Precision polishing system sample retention unit E type polishing device sample holding attachment-Musashino Denshi, INC.

Precision polishing system sample retention unit E type polishing device sample holding attachment

Musashino Denshi, INC.

5.0

270+ people viewing

Last viewed: 5 hours ago

Response time: 4.65 hours

Chemical Mechanical Polishing (CMP) Machines

3 models listed

Autumn chuck type holder can be automatically polished with set polishing amount-Musashino Denshi, INC.

Autumn chuck type holder can be automatically polished with set polishing amount

Musashino Denshi, INC.

5.0

320+ people viewing

Last viewed: 2 hours ago

Response time: 4.65 hours

Vacuum Clamps

6 models listed

Automatic polishing of the set polished amount can be polished high -precision holder-Musashino Denshi, INC.

Automatic polishing of the set polished amount can be polished high -precision holder

Musashino Denshi, INC.

5.0

470+ people viewing

Last viewed: 5 hours ago

Response time: 4.65 hours

Jig Parts

5 models listed

Automatic polishing work is possible TEM holder-Musashino Denshi, INC.

Automatic polishing work is possible TEM holder

Musashino Denshi, INC.

5.0

310+ people viewing

Last viewed: 3 hours ago

Response time: 4.65 hours

Jig Parts
Realize easy cutting to samples Precision blade cutting machine MPC-130-Musashino Denshi, INC.

Realize easy cutting to samples Precision blade cutting machine MPC-130

Musashino Denshi, INC.

5.0

410+ people viewing

Last viewed: 5 hours ago

Response time: 4.65 hours

Desktop Cutting Machines

3 models listed

Realize the work that does not rely on human power SC-100-Musashino Denshi, INC.

Realize the work that does not rely on human power SC-100

Musashino Denshi, INC.

5.0

240+ people viewing

Last viewed: 5 hours ago

Response time: 4.65 hours

Desktop Cutting Machines

3 models listed

Adjustable amount of polishing with a minimum of 10 μm scale adjustment holder-Musashino Denshi, INC.

Adjustable amount of polishing with a minimum of 10 μm scale adjustment holder

Musashino Denshi, INC.

5.0

400+ people viewing

Last viewed: 10 minutes ago

Response time: 4.65 hours

Jig Parts

2 models listed

Precision and polishing system custom polishing device Panel type Sample CMP polishing device MA-600E RECT-Musashino Denshi, INC.

Precision and polishing system custom polishing device Panel type Sample CMP polishing device MA-600E RECT

Musashino Denshi, INC.

5.0

580+ people viewing

Last viewed: 54 minutes ago

Response time: 4.65 hours

Automatic Titrators

3 models listed

Diamond wire saw CS-203 can be cut in both wet and dry type-Musashino Denshi, INC.

Diamond wire saw CS-203 can be cut in both wet and dry type

Musashino Denshi, INC.

5.0

320+ people viewing

Last viewed: 5 hours ago

Response time: 4.65 hours

Diamond Saws

4 models listed


View more products of Musashino Denshi, INC.

About Company Handling This Product

Musashino Denshi, INC.

Response Rate

100.0%

Response Time

4.6hrs

Company Review

5.0

Company Overview

Musashino Denshi, INC., established in 1977 and based in Japan, is a manufacturer of grinding and polishing ma...

See More

  • Japan

This is the version of our website addressed to speakers of English in the United States. If you are a resident of another country, please select the appropriate version of Metoree for your country in the drop-down menu.

Copyright © 2024 Metoree