Black leather board HTi10Handling Company
Maruichi Carbide Co., Ltd.Categories
Click on the part number for more information about each product
| Image | Part Number | Price (excluding tax) | Toughness (MPa m1/2) | Particle size full | Hardness (HRA) | Specific gravity | Transverse rupture strength (GPa) | Size | ISO | Hv Vickers (ISO 3878) | HRC Rockwell C | Co amount |
|---|---|---|---|---|---|---|---|---|---|---|---|---|
|
|
Black leather board HTi10 (2mm) |
Available upon quote |
6.8 |
Less than 1.0μm |
92 |
14.9 |
3.2 |
2×2×120~2×20×120 |
K10 equivalent product |
1,700 |
78.1 |
6mass% |
|
|
Black leather board HTi10 (2.5mm) |
Available upon quote |
6.8 |
Less than 1.0μm |
92 |
14.9 |
3.2 |
2.5×3×120~2.5×15×120 |
K10 equivalent product |
1,700 |
78.1 |
6mass% |
|
|
Black leather board HTi10 (3mm) |
Available upon quote |
6.8 |
Less than 1.0μm |
92 |
14.9 |
3.2 |
3×3×120~3×26×120 |
K10 equivalent product |
1,700 |
78.1 |
6mass% |
|
|
Black leather board HTi10 (3.5mm) |
Available upon quote |
6.8 |
Less than 1.0μm |
92 |
14.9 |
3.2 |
3.5×4×120~3.5×15×120 |
K10 equivalent product |
1,700 |
78.1 |
6mass% |
|
|
Black leather board HTi10 (4mm) |
Available upon quote |
6.8 |
Less than 1.0μm |
92 |
14.9 |
3.2 |
4×4×120~4×30×120 |
K10 equivalent product |
1,700 |
78.1 |
6mass% |
|
|
Black leather board HTi10 (5mm) |
Available upon quote |
6.8 |
Less than 1.0μm |
92 |
14.9 |
3.2 |
5×5×125~5×20×120 |
K10 equivalent product |
1,700 |
78.1 |
6mass% |
|
|
Black leather board HTi10 (6mm) |
Available upon quote |
6.8 |
Less than 1.0μm |
92 |
14.9 |
3.2 |
6×6×125,6×10×120 |
K10 equivalent product |
1,700 |
78.1 |
6mass% |
|
|
Black leather board HTi10 (8mm) |
Available upon quote |
6.8 |
Less than 1.0μm |
92 |
14.9 |
3.2 |
8×8×125 |
K10 equivalent product |
1,700 |
78.1 |
6mass% |
Click on the part number for more information about each product
Reviews shown here are reviews of companies.
Reviews shown here are reviews of companies.
Response Rate
100.0%
Response Time
0.3hrs