■ Overview Aqueous white ceramic coating agent. Silica (SIO2) is the main ingredient and forms a white and smooth film. Applying, dipping, spraying and drying to the metal surface creates a hard -to -heat -resistant (heat -resistant upper limit of 1,100 ° C), corrosion resistance, electrical insulation, and chemical resistance. The film expansion coefficient is almost equal to steel and is suitable for steel and stainless steel coating. ■ Characteristics ・ It is easy to apply, and it is easy to coat with brush, brush application and dipping. ・ You can use a spray gun for paint to use a spray coating or dispenser to make local coating. ・ Since the surface of the generated ceramic film is smooth, it has a separation effect at high temperature. ・ Since high -purity silica fine particles are used, it can also be used for coating precision metal parts. ・ If you cure, you will form a film only for inorganic substances, and there is no gas outbreak in the vacuum, inert gas. It can also be used in true roses and reduced atmosphere. ・ After coating, when the film is low humidity or at high temperature, it is only necessary to dry at room temperature and do not need cure. ・ Because it is single -liquid, there is no need to mix. ■ Use ・ For steel and stainless steel parts, heat -resistant corrosion and insulation coatin. ・ For racks, bats, radol, and racks, heat resistance, drug -resistant coating. ・ For duct, food, protection coating inside the chimney. ・ Coating the metal part in the vacuum furnace. ・ For protective coating of soldering and jigs. ・ As a coating agent for heat -resistant type. ■ About cure (firing) processing Sera coat 22 is dried at room temperature, and if you put it in a high temperature and low humidity atmosphere, the atmosphere will be cure, so you do not need to be particularly cure, but if you do not do cure, it will be moisturized. remain. If you have a high humidity atmosphere, please cure in the following steps. In the case of thick coating, increase the cure time as appropriate. After drying at room temperature for 2 hours, fired at 95 ° C for 3 hours and fired for 1 hour at 150 ° C.
You can search for other models from each index. The displayed value is the value of the currently selected part number.
Cure shrinkage
Effective storage period
Heat -resistant shock
Heat expansion coefficient
Heatproof temperature
Insulated destructive voltage (KV/mm)
Main binder (binding agent)
Main ingredient (filler)
PH
Processing area per 1L (M^2/L)
Standard film thickness
The hardness of the generated film (Morse)
Volume-specific resistance (OHM-CM, room temperature)
capacity
chemical resistance
color
Firing temperature
Particle size (μ)
Part Number
Sera coat 22Handling Company
Edec Co., Ltd.Categories
Image | Price (excluding tax) | Cure shrinkage | Effective storage period | Heat -resistant shock | Heat expansion coefficient | Heatproof temperature | Insulated destructive voltage (KV/mm) | Main binder (binding agent) | Main ingredient (filler) | PH | Processing area per 1L (M^2/L) | Standard film thickness | The hardness of the generated film (Morse) | Volume-specific resistance (OHM-CM, room temperature) | capacity | chemical resistance | color |
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
![]() |
Available upon quote | 0.40% | Six months | Slightly good | 11.2x10^-6 | 1,000 ° C (continuation), 1,100 ° C (intermittent) | 1.5 | Coloydar Silica | Silica (purity 99.78%) | 10-12 | 3 ~ 4 | 0.25mm | 5 | 10^9 | 1L, 1 Gallon (approximately 4L) Popular poly container | It has acid resistance except for oil -resistant, solvent, alkaline resistance, and fluffy acid (but be careful as liquids and gas permeate). | White |