Bending strength 20° (Mpa)
Bulk density ( g/cm3)
Color
Dielectric constant 1MHz
Dielectric constant 3GHz
Dielectric strength (kV/mm)
Fracture toughness (Mpa･m1/2)
Hardness (HV) (Gpa)
Linear expansion coefficient RT~200℃ ( ×10^-6/℃)
Linear expansion coefficient RT~600℃
Linear expansion coefficient RT~800℃
Main component
Poisson's ratio
Specific heat RT ( J/ ( kg･K) )
Thermal conductivity 20℃ ( W/ ( m･K) )
Thermal shock resistance (℃)
Volume resistivity 20℃ (Ω･cm)
Young's modulus (Gpa)
Compressive strength (Mpa)
Dissipation factor 1MHz ( ×10^-4)
Dissipation factor 3GHz ( ×10^-4)
Maximum operating temperature Oxidizing atmosphere (℃)
Part Number
96% aluminaHandling Company
Shimizu Shokai Co., Ltd.Categories
| Image | Price (excluding tax) | Bending strength 20° (Mpa) | Bulk density ( g/cm3) | Color | Compressive strength (Mpa) | Dielectric constant 1MHz | Dielectric strength (kV/mm) | Fracture toughness (Mpa･m1/2) | Hardness (HV) (Gpa) | Linear expansion coefficient RT~200℃ ( ×10^-6/℃) | Linear expansion coefficient RT~600℃ | Linear expansion coefficient RT~800℃ | Main component | Maximum operating temperature Oxidizing atmosphere (℃) | Poisson's ratio | Specific heat RT ( J/ ( kg･K) ) | Thermal conductivity 20℃ ( W/ ( m･K) ) | Thermal shock resistance (℃) | Volume resistivity 20℃ (Ω･cm) | Young's modulus (Gpa) |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
|
|
Available upon quote | 320 | 4 | White | 2,100 | 9.5 | 10 | 3.5 | 13 | 7.3 | 7.8 | 8 | Al2O3 96 | 1,500 | 0.23 | 780 | Twenty one | 150 | >10^14 | 300 |