2-component acrylic primer super primer for aliphatic/aromatic nylon materialsHandling Company
Musashi Paint Co., Ltd.Categories
| Image | Part Number | Price (excluding tax) | Pencil hardness | Mixing ratio Paint: Hardener: Thinner (weight ratio) | Migration resistance | Heat resistance | Moisture resistance | Abrasion resistant eraser | Wear resistant jeans | Low temperature resistance | Heat cycle resistance | Alcohol resistance | Standard film thickness | Adhesion | Paint viscosity (Iwata simple viscometer NK-2,20℃) | Painting method Spray pressure | Painting method Gun caliber | Drying conditions Drying temperature x time | Drying conditions Setting temperature x time | Spray gun and object distance |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
8954 |
Available upon quote |
Pencil scratch tester, Mitsubishi Uni, load 1kg, scratch method [2H] |
10:1:8±1 |
Foamed polyethylene, load 80g/cm2, 60℃, 48 hours, no appearance abnormality [Passed] |
Adhesion test after being left at 85℃ for 96 hours [100/100] |
40℃×98%RH×Adhesion test after 48 hours [100/100] |
Sony eraser tester, load 1.64kgf, 300 times, no substrate exposure [Passed] |
Rubbing test, load 500g/cm2, 2000 reciprocations, no substrate exposure [Passed] |
Adhesion test after being left at -40℃ for 96 hours [100/100] |
-20℃×3 hours ⇔ 60℃×3 hours, adhesion test after 10 cycles [100/100] |
99.5% ethanol rubbing, load 500g/cm2,500 times, no exposed substrate [Passed] |
12±2μm |
1mm square grid Cellotape peeling test (10×10) [100/100] |
10±2 seconds |
0.3±0.1MPa |
1.3±0.3mmφ |
80℃×30 minutes |
25℃×5 minutes |
25±5cm |