1-component baking acrylic urethane paint for metals EcometaldoHandling Company
Musashi Paint Co., Ltd.Categories
| Image | Part Number | Price (excluding tax) | Pencil hardness | Mixing ratio Paint: Thinner (weight ratio) | Acid resistance | Heat resistance | Moisture resistance | Eraser abrasion resistance | Boiling water resistance | Weather resistance | Heat cycle resistance | Alcohol resistance | Alkali resistance | Standard film thickness | Adhesion | Paint viscosity (Iwata simple viscometer NK-2,20℃) | Painting method Spray pressure | Painting method Gun caliber | Drying conditions Drying temperature x time | Drying conditions Setting temperature x time | Spray gun and object distance |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
EC-GB31 |
Available upon quote |
Pencil scratch tester, Mitsubishi Pencil Uni, load 1kg, scratch method [2H] |
100:70±10 |
5% HCl, room temperature x 24 hours, no abnormal appearance [Passed] |
Adhesion test after being left at 85℃ for 96 hours [Passed] |
50℃×98%RH×Adhesion test after being left for 120 hours [100/100] |
Sony eraser tester, load 1.64kgf, 300 times, no substrate exposure [Passed] |
Adhesion test after 1 hour immersion in boiling water (98℃) [100/100] |
Sunshine weather meter, 150 hours, color difference ⊿E=1.0 or less [Passed] |
-30℃×1 hour ⇔ 60℃×1 hour, adhesion test after 10 cycles [100/100] |
99.5% ethanol rubbing, 500g/cm2, 100 times, no substrate exposure [Passed] |
5% NaOH, room temperature x 24 hours, no abnormal appearance [Passed] |
20±5μm |
1mm square grid Cellotape peeling test (10×10) [100/100] |
10±2 seconds |
0.3±0.1MPa |
1.3±0.3mmφ |
160℃×20 minutes |
25℃×5 minutes |
25±5cm |