Ultraviolet curing paint Eco Ultra Vine EC-UV90Handling Company
Musashi Paint Co., Ltd.Categories
Items marked with have different values depending on the model number.
Click on the part number for more information about each product
| Product Image | Part Number | Price (excluding tax) | Abrasion resistant eraser | Adhesion | Alcohol resistance | Curing conditions Cumulative light intensity | Curing conditions Lamp output | Curing conditions Lamp type | Curing conditions Peak illuminance | Curing conditions Pre-drying temperature x time | Heat cycle resistance | Heat resistance | Low temperature resistance | Migration resistance | Mixing ratio Paint: Thinner (weight ratio) | Moisture resistance | Paint viscosity (Iwata simple viscometer NK-2,20℃) | Painting method Gun caliber | Painting method Spray pressure | Pencil hardness | Spray gun and object distance | Standard film thickness | Sunscreen resistance | Wear resistant jeans |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
EC-UV90 |
Available upon quote | Sony eraser tester, load 1.64kgf, 300 times, no substrate exposure [Passed] | 1mm square grid Cellotape peeling test (10×10) [100/100] | 99.5% ethanol rubbing, load 500g/cm2,500 times, no exposed substrate [Passed] |
800±100mj/cm2 *Measured using EYE UV METER UVPF-A1 (light receiving section PD-365 manufactured by EYE GRAPHICS Co., Ltd.) |
100±20W/cm | High pressure mercury lamp |
100±20mW/cm2 *Measured using EYE UV METER UVPF-A1 (light receiving section PD-365 manufactured by EYE GRAPHICS Co., Ltd.) |
60℃×5 minutes | -20℃×3 hours ⇔ 60℃×3 hours, adhesion test after 10 cycles [100/100] | Adhesion test after being left at 85℃ for 240 hours [100/100] | Adhesion test after being left at -40℃ for 96 hours [100/100] | Foamed polyethylene, load 80g/cm2, 60℃, 48 hours, no appearance abnormality [Passed] | 100:80±10 | Adhesion test after 80℃×98%RH×240 hours [100/100] | 8.5±0.5 seconds | 1.3±0.3mmφ | 0.3±0.1MPa | Pencil scratch tester, Mitsubishi Uni, load 1kg, scratch method [F~H] | 25±5cm | 17±2μm | Sunscreen 2.0g/dm2 After leaving at 80℃ for 4 hours, adhesion test [passed] | Rubbing test, load 500g/cm2, 2000 reciprocations, no substrate exposure [Passed] | |
EC-UV90-RP |
Available upon quote | Sony eraser tester, load 1.64kgf, 300 times, no substrate exposure [Passed] | 1mm square grid Cellotape peeling test (10×10) [100/100] | 99.5% ethanol rubbing, load 500g/cm2,500 times, no exposed substrate [Passed] |
800±100mj/cm2 *Measured using EYE UV METER UVPF-A1 (light receiving section PD-365 manufactured by EYE GRAPHICS Co., Ltd.) |
100±20W/cm | High pressure mercury lamp |
100±20mW/cm2 *Measured using EYE UV METER UVPF-A1 (light receiving section PD-365 manufactured by EYE GRAPHICS Co., Ltd.) |
60℃×5 minutes | -20℃×3 hours ⇔ 60℃×3 hours, adhesion test after 10 cycles [100/100] | Adhesion test after being left at 85℃ for 240 hours [100/100] | Adhesion test after being left at -40℃ for 96 hours [100/100] | Foamed polyethylene, load 80g/cm2, 60℃, 48 hours, no appearance abnormality [Passed] | 100:80±10 | Adhesion test after 80℃×98%RH×240 hours [100/100] | 8.5±0.5 seconds | 1.3±0.3mmφ | 0.3±0.1MPa | Pencil scratch tester, Mitsubishi Uni, load 1kg, scratch method [F~H] | 25±5cm | 17±2μm | Sunscreen 2.0g/dm2 After leaving at 80℃ for 4 hours, adhesion test [passed] | Rubbing test, load 500g/cm2, 2000 reciprocations, no substrate exposure [Passed] |