Environmentally friendly 2-component acrylic urethane self-healing paint for plastics Eco Arbus UrexHandling Company
Musashi Paint Co., Ltd.Categories
Click on the part number for more information about each product
| Image | Part Number | Price (excluding tax) | Pencil hardness | Mixing ratio Paint: Hardener: Thinner (weight ratio) | Acid resistance | Heat resistance | Moisture resistance | Eraser abrasion resistance | Weather resistance | Heat cycle resistance | Alcohol resistance | Alkali resistance | Scratch resistance | Standard film thickness | Adhesion | Paint viscosity (Iwata simple viscometer NK-2,20℃) | Painting method Spray pressure | Painting method Gun caliber | Drying conditions Drying temperature x time | Drying conditions Setting temperature x time | Spray gun and object distance |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
EC-AX620 |
Available upon quote |
Pencil scratch tester, Mitsubishi Pencil Uni, load 1kg, scratch method [HB] |
2:1:2±1 |
0.1N H2SO4, 5cc, room temperature x 24 hours, no abnormality in appearance [Passed] |
Adhesion test after being left at 85℃ for 96 hours [100/100] |
Adhesion test after 50℃×98%RH×120 hours [100/100] |
Sony eraser tester, load 1.64kgf, 100 times, no substrate exposure [Passed] |
Sunshine weather meter, 150 hours, color difference ⊿E=1.0 or less [Passed] |
-20℃×3 hours ⇔ 60℃×3 hours, adhesion test after 10 cycles [100/100] |
99.5% ethanol rubbing, 500g/cm2, 100 times, no substrate exposure [Passed] |
0.1N NaOH, 5cc, 55℃ x 4 hours, no abnormality in appearance [Passed] |
Uses glass beads, load 21.6N, 50 cycles ⊿E≦1.0, gloss retention rate: within 160% [Pass] |
23±3μm |
1mm square grid Cellotape peeling test (10×10) [100/100] |
10±1 seconds |
0.3±0.1MPa |
1.3±0.3mmφ |
80℃×30 minutes |
25℃×5 minutes |
25±5cm |
|
EC-AX62 |
Available upon quote |
Pencil scratch tester, Mitsubishi Pencil Uni, load 1kg, scratch method [HB] |
2:1:2±1 |
0.1N H2SO4, 5cc, room temperature x 24 hours, no abnormality in appearance [Passed] |
Adhesion test after being left at 85℃ for 96 hours [100/100] |
Adhesion test after 50℃×98%RH×120 hours [100/100] |
Sony eraser tester, load 1.64kgf, 100 times, no substrate exposure [Passed] |
Sunshine weather meter, 150 hours, color difference ⊿E=1.0 or less [Passed] |
-20℃×3 hours ⇔ 60℃×3 hours, adhesion test after 10 cycles [100/100] |
99.5% ethanol rubbing, 500g/cm2, 100 times, no substrate exposure [Passed] |
0.1N NaOH, 5cc, 55℃ x 4 hours, no abnormality in appearance [Passed] |
Uses glass beads, load 21.6N, 50 cycles ⊿E≦1.0, gloss retention rate: within 160% [Pass] |
23±3μm |
1mm square grid Cellotape peeling test (10×10) [100/100] |
10±1 seconds |
0.3±0.1MPa |
1.3±0.3mmφ |
80℃×30 minutes |
25℃×5 minutes |
25±5cm |