Environmentally friendly 1-component acrylic lacquer paint for plastics Ecopla Ace
Musashi Paint Co., Ltd.
About This Product
■Summary
"Ecopla Ace EC-FJ50-", like the conventional "EC-MX50-", has good aluminum pigment orientation, and has excellent brightness and design that can be used not only for home appliances but also for high-brightness metallic colors for car interiors. This is a product that has been designed. This is an environmentally friendly (toluene and xylene free) acrylic lacquer paint with particularly improved sunscreen resistance in terms of physical properties.
■Features
・BTX-free paint
・High brightness
・Good painting workability
・Excellent sunscreen resistance
■Recommended thinner
・Z-EC-B343 Ecopla Ace Thinner (Quick-drying type)
・Z-EC-B345 Ecopla Ace Thinner (Standard type)
・Z-EC-B347 Ecopla Ace Thinner (Slow drying type)
■Applicable materials
・ABS
・PC
・PC/ABS
■Precautions for use
- If foreign substances such as mold release agents adhere to the material, it may cause poor adhesion or repellency, so please wash it before painting.
・Depending on the type of solvent, thinner may cause a decline in physical properties, so be sure to use a dedicated thinner.
- Various grades of materials are available, and their properties may differ from the original, so please check before using.
・Be sure to stir evenly before use. When painting, put the diluted paint in a stirring tank and paint while stirring.
- Avoid direct sunlight and store paint in a cool, dark place (-20 to 40℃).
-
Product
Environmentally friendly 1-component acrylic lacquer paint for plastics Ecopla Ace
-
Handling Company
Musashi Paint Co., Ltd.
-
Categories
1 Models of Environmentally friendly 1-component acrylic lacquer paint for plastics Ecopla Ace
| Product Image | Part Number | Price (excluding tax) | Adhesion | Alcohol resistance | Drying conditions Drying temperature x time | Drying conditions Setting temperature x time | Eraser abrasion resistance | Heat cycle resistance | Heat resistance | Mixing ratio Paint: Thinner (weight ratio) | Moisture resistance | Oil and fat resistance | Paint viscosity (Iwata simple viscometer NK-2,20℃) | Painting method Gun caliber | Painting method Spray pressure | Pencil hardness | Spray gun and object distance | Standard film thickness | Sunscreen resistance | Weather resistance |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
EC-FJ50 |
Available upon quote | 1mm square grid Cellotape peeling test (10×10) [100/100] | 99.5% ethanol rubbing, load 500g/cm2, 100 cycles, no substrate exposure [Passed] | 60℃×30 minutes | 25℃×5 minutes | Sony eraser tester, load 1.64kgf, 900 times, no substrate exposure [Passed] | -20℃×3 hours ⇔ 60℃×3 hours, adhesion test after 10 cycles [100/100] | Adhesion test after being left at 85℃ for 96 hours [100/100] | 100:130±10 | 40℃×98%RH×Adhesion test after being left for 48 hours [100/100] | Castor oil, 40℃ x 90% x Adhesion test after being left for 24 hours [100/100] | 10±1 seconds | 1.3±0.3mmφ | 0.3±0.1MPa | Pencil scratch tester, Mitsubishi Uni, load 1kg, scratch method [F] | 25±5cm | 13±2μm | Sunscreen 2.0g/dm2, adhesion test after leaving at 55℃ for 4 hours [Passed] | Sunshine weather meter, 600 hours, color difference ⊿E=1.0 or less [Passed] |