New sensory expression paint Next-generation highly durable 2-component soft-feel paint for plastics Neo Lavasan Soft
Musashi Paint Co., Ltd.

⚙️ Plastic & Rubber Manufacturing

About This Product

■Summary

Soft feel paints are introduced by various companies as paints that give a soft feel to the touch and to the eyes, and the soft feel paints Lavasan and Peach Skin are paints that have excellent touch and workability. ``Neorabasan Soft NS781-Line'' is a soft-feel paint that, like Neorabasan, solves the problem of hydrolysis resistance while giving it an even more tactile feel.

■Features

・Excellent hydrolysis resistance ・Excellent scratch resistance ・Can be colored with 1 coat ・Fast curing and drying ・Excellent painting workability due to long pot life ・Recoatable Recommended thinners and hardeners thinner

■For ABS

・Z-29625 Lavasan thinner (standard type) ・Z-29626 Lavasan thinner (slow drying type)

■For PC, PC/ABS

・Z-29585 Lavasan thinner (standard type)

■Hardening agent

・Z-H-760

■Applicable materials and undercoating

・ABS ・PC ・PC/ABS ・P79-,UNP79-line (2-component acrylic urethane paint) ・787-Line (2-component acrylic silicone paint)

■Precautions for use

- If foreign substances such as mold release agents adhere to the material, it may cause poor adhesion or repellency, so please wash it before painting. ・Depending on the type of solvent, thinner may cause a decline in physical properties, so be sure to use a dedicated thinner. - Various grades of materials are available, and their properties may differ from the original, so please check before using. ・Be sure to stir evenly before use. When painting, put the diluted paint in a stirring tank and paint while stirring. - Avoid direct sunlight and store paint in a cool, dark place (-20 to 40℃). ・Since it is a two-component paint, please make only the amount you need. Pot life is 4 hours at 20℃. Please note that if it exceeds its pot life, it may not be able to achieve its original performance.

  • Product

    New sensory expression paint Next-generation highly durable 2-component soft-feel paint for plastics Neo Lavasan Soft
  • Usage Scenarios

    Plastic & Rubber Manufacturing

Share this product


220+ people viewing


Free
Get started with our free quotation service - no cost, no obligation.

No Phone Required
We respect your privacy. You can receive quotes without sharing your phone number.

2 Models of New sensory expression paint Next-generation highly durable 2-component soft-feel paint for plastics Neo Lavasan Soft

Click on the part number for more information about each product

Image Part Number Price (excluding tax) Pencil hardness Mixing ratio Paint: Hardener: Thinner (weight ratio) Acid resistance Heat resistance Moisture resistance Eraser abrasion resistance Hydrolysis resistance Weather resistance Heat cycle resistance Alcohol resistance Alkali resistance Standard film thickness Adhesion Paint viscosity (Iwata simple viscometer NK-2,20℃) Painting method Spray pressure Painting method Gun caliber Drying conditions Drying temperature x time Drying conditions Setting temperature x time Spray gun and object distance

NS78100

Available upon quote

Pencil scratch tester, Mitsubishi Uni, load 1kg, scratch method [H]

10:1:5±1

0.1N H2SO4, 5cc, room temperature x 24 hours, no abnormality in appearance [Passed]

Adhesion test after 80℃ x 120 hours [100/100]

Adhesion test after 50℃×98%RH×120 hours [100/100]

Sony eraser tester, load 1.64kgf, 100 times, no substrate exposure [Passed]

80℃×90%RH×2000 hours, initial pencil hardness maintained [Passed]

Sunshine weather meter, 300 hours, color difference ⊿E=1.0 or less [Passed]

-30℃×3 hours ⇔ 60℃×3 hours, adhesion test after 10 cycles [100/100]

99.5% ethanol rubbing, 500g/cm2, 100 times, no substrate exposure [Passed]

0.1N NaOH, 5cc, 55℃ x 4 hours, no abnormality in appearance [Passed]

30±5μm

1mm square grid Cellotape peeling test (10×10) [100/100]

12±1 seconds

0.3±0.1MPa

1.3±0.3mmφ

70℃×30 minutes

25℃×10 minutes

25±5cm

NS781

Available upon quote

Pencil scratch tester, Mitsubishi Uni, load 1kg, scratch method [H]

10:1:5±1

0.1N H2SO4, 5cc, room temperature x 24 hours, no abnormality in appearance [Passed]

Adhesion test after 80℃ x 120 hours [100/100]

Adhesion test after 50℃×98%RH×120 hours [100/100]

Sony eraser tester, load 1.64kgf, 100 times, no substrate exposure [Passed]

80℃×90%RH×2000 hours, initial pencil hardness maintained [Passed]

Sunshine weather meter, 300 hours, color difference ⊿E=1.0 or less [Passed]

-30℃×3 hours ⇔ 60℃×3 hours, adhesion test after 10 cycles [100/100]

99.5% ethanol rubbing, 500g/cm2, 100 times, no substrate exposure [Passed]

0.1N NaOH, 5cc, 55℃ x 4 hours, no abnormality in appearance [Passed]

30±5μm

1mm square grid Cellotape peeling test (10×10) [100/100]

12±1 seconds

0.3±0.1MPa

1.3±0.3mmφ

70℃×30 minutes

25℃×10 minutes

25±5cm

Click on the part number for more information about each product

Customers who viewed this product also viewed

Reviews shown here are reviews of companies.

See More Coated Materials Products

About Company Handling This Product

This is the version of our website addressed to speakers of English in the United States. If you are a resident of another country, please select the appropriate version of Metoree for your country in the drop-down menu.

Copyright © 2025 Metoree