High brightness 2-component acrylic urethane paint for molded plastic Hiurex P Grande BonheurHandling Company
Musashi Paint Co., Ltd.Categories
Usage Scenarios
Plastic & Rubber Manufacturing| Image | Part Number | Price (excluding tax) | Pencil hardness | Mixing ratio Paint: Hardener: Thinner (weight ratio) | Acid resistance | Heat resistance | Moisture resistance | Eraser abrasion resistance | Weather resistance | Heat cycle resistance | Gasoline resistance | Alcohol resistance | Alkali resistance | Standard film thickness | Adhesion | Paint viscosity (Iwata simple viscometer NK-2,20℃) | Painting method Spray pressure | Painting method Gun caliber | Drying conditions Drying temperature x time | Drying conditions Setting temperature x time | Spray gun and object distance |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
GPX79 |
Available upon quote |
Pencil scratch tester, Mitsubishi Pencil Uni, load 1kg, scratch method [F] |
10:1:11±1 |
0.1N H2SO4, 5cc, room temperature x 24 hours, no abnormality in appearance [Passed] |
Adhesion test after being left at 85℃ for 96 hours [100/100] |
Adhesion test after 50℃×98%RH×120 hours [100/100] |
Sony eraser tester, load 1.64kgf, 100 times, no substrate exposure [Passed] |
Sunshine weather meter, 300 hours, color difference ⊿E=1.0 or less [Passed] |
-20℃×3 hours ⇔ 60℃×3 hours, adhesion test after 10 cycles [100/100] |
Regular gasoline, immersed for 30 minutes, no abnormalities in appearance [Passed] |
99.5% ethanol rubbing, 500g/cm2, 100 times, no substrate exposure [Passed] |
0.1N NaOH, 5cc, 55℃ x 4 hours, no abnormality in appearance [Passed] |
9±1μm |
1mm square grid Cellotape peeling test (10×10) [100/100] |
9±1 seconds |
0.3±0.1MPa |
1.3±0.3mmφ |
80℃×30 minutes |
25℃×5 minutes |
25±5cm |