| Image | Part Number | Price (excluding tax) | Applicable standards | Continuous use temperature | Color | Withstand voltage characteristic value | Withstanding voltage typical value | Hardness (Shore D) Typical value | Flammability characteristic value | Specific gravity typical value | Material | Tensile strength characteristic value | Tensile strength typical value | Nominal size (mm) | Water absorption characteristic value | Water absorption typical value | Shrinkage rate Length change rate | Shrinkage rate Inner diameter shrinkage rate | Shrinkage temperature | Size after shrinkage Wall thickness (reference value) (mm) | Size after shrinkage Inner diameter (maximum value) (mm) | Size before shrinkage Wall thickness (reference value) (mm) | Size before shrinkage Inner diameter (mm) | Single length (minimum) Cut product (m) | Single length (minimum) Reel (m) | Elongation characteristic value | Elongation typical value |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
Sumitube A 1.5×0.2 |
Available upon quote |
Sumitomo Electric Fine Polymer Specification (Specification No. R4-0180) |
-55~105℃ |
11 colors available |
AC2.5kV x 60 seconds, no destruction |
Passed |
42 |
Flammable |
0.92 |
Electron beam crosslinked soft polyolefin resin |
10.4MPa or more |
19.2MPa |
1.5×0.2 |
23℃×24 hours, 0.10% or less |
0.09% |
-15% or more |
Approximately 40% |
115℃ or higher |
0.40±0.10 |
0.8 |
0.2 |
2.10±0.30 |
1 |
200 |
200% or more |
440% |
|
Sumitube A 2×0.2 |
Available upon quote |
Sumitomo Electric Fine Polymer Specification (Specification No. R4-0180) |
-55~105℃ |
11 colors available |
AC2.5kV x 60 seconds, no destruction |
Passed |
42 |
Flammable |
0.92 |
Electron beam crosslinked soft polyolefin resin |
10.4MPa or more |
19.2MPa |
2×0.2 |
23℃×24 hours, 0.10% or less |
0.09% |
-15% or more |
Approximately 40% |
115℃ or higher |
0.40±0.10 |
1.3 |
0.2 |
2.60±0.30 |
1 |
200 |
200% or more |
440% |
|
Sumitube A 2.5×0.2 |
Available upon quote |
Sumitomo Electric Fine Polymer Specification (Specification No. R4-0180) |
-55~105℃ |
11 colors available |
AC2.5kV x 60 seconds, no destruction |
Passed |
42 |
Flammable |
0.92 |
Electron beam crosslinked soft polyolefin resin |
10.4MPa or more |
19.2MPa |
2.5×0.2 |
23℃×24 hours, 0.10% or less |
0.09% |
-15% or more |
Approximately 40% |
115℃ or higher |
0.40±0.10 |
1.5 |
0.2 |
3.10±0.30 |
1 |
200 |
200% or more |
440% |
|
Sumitube A 3×0.2 |
Available upon quote |
Sumitomo Electric Fine Polymer Specification (Specification No. R4-0180) |
-55~105℃ |
11 colors available |
AC2.5kV x 60 seconds, no destruction |
Passed |
42 |
Flammable |
0.92 |
Electron beam crosslinked soft polyolefin resin |
10.4MPa or more |
19.2MPa |
3×0.2 |
23℃×24 hours, 0.10% or less |
0.09% |
-15% or more |
Approximately 40% |
115℃ or higher |
0.40±0.10 |
1.8 |
0.2 |
3.60±0.30 |
1 |
200 |
200% or more |
440% |
|
Sumitube A 3.5×0.2 |
Available upon quote |
Sumitomo Electric Fine Polymer Specification (Specification No. R4-0180) |
-55~105℃ |
11 colors available |
AC2.5kV x 60 seconds, no destruction |
Passed |
42 |
Flammable |
0.92 |
Electron beam crosslinked soft polyolefin resin |
10.4MPa or more |
19.2MPa |
3.5×0.2 |
23℃×24 hours, 0.10% or less |
0.09% |
-15% or more |
Approximately 40% |
115℃ or higher |
0.40±0.10 |
2 |
0.2 |
4.10±0.30 |
1 |
100 |
200% or more |
440% |
|
Sumitube A 4×0.2 |
Available upon quote |
Sumitomo Electric Fine Polymer Specification (Specification No. R4-0180) |
-55~105℃ |
11 colors available |
AC2.5kV x 60 seconds, no destruction |
Passed |
42 |
Flammable |
0.92 |
Electron beam crosslinked soft polyolefin resin |
10.4MPa or more |
19.2MPa |
4×0.2 |
23℃×24 hours, 0.10% or less |
0.09% |
-15% or more |
Approximately 40% |
115℃ or higher |
0.40±0.10 |
2.3 |
0.2 |
4.60±0.30 |
1 |
100 |
200% or more |
440% |
|
Sumitube A 5×0.2 |
Available upon quote |
Sumitomo Electric Fine Polymer Specification (Specification No. R4-0180) |
-55~105℃ |
11 colors available |
AC2.5kV x 60 seconds, no destruction |
Passed |
42 |
Flammable |
0.92 |
Electron beam crosslinked soft polyolefin resin |
10.4MPa or more |
19.2MPa |
5×0.2 |
23℃×24 hours, 0.10% or less |
0.09% |
-15% or more |
Approximately 40% |
115℃ or higher |
0.40±0.10 |
2.9 |
0.2 |
5.60±0.30 |
1 |
100 |
200% or more |
440% |
|
Sumitube A 6×0.25 |
Available upon quote |
Sumitomo Electric Fine Polymer Specification (Specification No. R4-0180) |
-55~105℃ |
11 colors available |
AC2.5kV x 60 seconds, no destruction |
Passed |
42 |
Flammable |
0.92 |
Electron beam crosslinked soft polyolefin resin |
10.4MPa or more |
19.2MPa |
6×0.25 |
23℃×24 hours, 0.10% or less |
0.09% |
-15% or more |
Approximately 40% |
115℃ or higher |
0.50±0.10 |
3.5 |
0.25 |
6.5±0.3 |
1 |
100 |
200% or more |
440% |
|
Sumitube A 7×0.25 |
Available upon quote |
Sumitomo Electric Fine Polymer Specification (Specification No. R4-0180) |
-55~105℃ |
11 colors available |
AC2.5kV x 60 seconds, no destruction |
Passed |
42 |
Flammable |
0.92 |
Electron beam crosslinked soft polyolefin resin |
10.4MPa or more |
19.2MPa |
7×0.25 |
23℃×24 hours, 0.10% or less |
0.09% |
-15% or more |
Approximately 40% |
115℃ or higher |
0.50±0.10 |
4.2 |
0.25 |
7.5±0.3 |
1 |
50 |
200% or more |
440% |
|
Sumitube A 8×0.25 |
Available upon quote |
Sumitomo Electric Fine Polymer Specification (Specification No. R4-0180) |
-55~105℃ |
11 colors available |
AC2.5kV x 60 seconds, no destruction |
Passed |
42 |
Flammable |
0.92 |
Electron beam crosslinked soft polyolefin resin |
10.4MPa or more |
19.2MPa |
8×0.25 |
23℃×24 hours, 0.10% or less |
0.09% |
-15% or more |
Approximately 40% |
115℃ or higher |
0.50±0.10 |
4.7 |
0.25 |
8.5±0.3 |
1 |
50 |
200% or more |
440% |
Click on the part number for more information about each product
Reviews shown here are reviews of companies.
Reviews shown here are reviews of companies.
Response Rate
100.0%
Response Time
56.0hrs