Ultra Thick Polycarbonate SheetHandling Company
Excelite Plastic Co.,LtdCategories
| Image | Part Number | Price (excluding tax) | Density (Test Method SO 1183-1) | Water absorption saturation (Test Conditions Water at 23°C ,Test Method ISO62) | Water absorption equilibrium (Test Conditions 23°C, 50% relative humidity,Test Method ISO 62) | Refractive index (Test Conditions Procedure A,Test Method ISO 489) | Tensile modulus (Test Conditions 1mm/min,Test Method ISO 527-1, -2) | Yield stress (Test Conditions 50mm/min,Test Method ISO 527-1, -2) | Yield strain (Test Conditions 50mm/min,Test Method ISO 527-1, -2) | Nominal strain at break (Test Conditions 50mm/min,Test Method ISO 527-1, -2) | Flexural modulus (Test Conditions 2mm/min,Test Method ISO 178:2019) | Flexural strength (Test Conditions 2mm/min,Test Method ISO 178:2019) | IZOD impact strength (Notched) (Test Conditions 23°C, 50% relative humidity, 3.2mm,Test Method ASTM D256-10 Method A) | VICAT Softening Temperature (Test Conditions 50N, 50K/h,Test Method ISO 306: 2013) | Thermal conductivity (Test Conditions 23°C,Test Method ISO 8302) | Electrical strength (Test Conditions 23±2°C, 50±5 % RH, 48h,Test Method IEC 60243 -1: 2013) | Volume resistivity (Test Method IEC 60231 -3: 2016) | Surface resistivity (Test Method IEC 60231 -3: 2016) |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
|
|
Ultra Thick Polycarbonate Sheet |
Available upon quote |
1.2g/cm3 |
0.3％ |
0.12％ |
1.587 |
2,300Mpa |
60Mpa |
6% |
50% |
2,410Mpa |
113Mpa |
921J/m |
145°C |
0.2W/mK |
14.29k/V/mm |
1.14E+15 Ω*m Ω*m |
3.18E+16 Ω/sq Ω/sq |
Reviews shown here are reviews of companies.
Reviews shown here are reviews of companies.