Pelcoat <Epoxy paint for electronics> Exterior paint for hybrid IC CE-55Handling Company
PelnoxCategories
| Image | Part Number | Price (excluding tax) | Properties after curing: Flame retardant | Characteristics after curing Dielectric constant | Characteristics after curing Dielectric loss tangent | Characteristics after curing Cotton expansion coefficient | Properties after curing Hardness | Properties after curing Flexural modulus | Properties after curing: Bending strength | Characteristics after curing Volume resistivity | Characteristics after curing Impurity ions | Characteristics after curing Glass transition temperature | Properties before curing Viscosity | Properties before curing Specific gravity | Properties before curing Appearance | Standard curing conditions | Packing form | Function | Category |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
|
|
CE-55 |
Available upon quote |
UL-94: V-0 certified |
JIS K 6911 25℃: 3.8 |
JIS K 6911 25℃: 0.4% |
Below Tg: 0.6 (10^-5/℃) |
JIS K-7215 25℃: 94 Shore D |
JIS K-6911 25℃: 9,800MPa |
JIS K-6911 25℃: 42MPa |
JIS K 6911 25℃：10^15 (Ω-cm) |
Grinding of cured product PCT (121℃, 2 atm) 24 hours Water extraction: Na+ 3ppm, Cl- 5ppm |
TMA method: 140℃ |
25℃: 8,000mPa・s |
25℃: 1.64 |
Visual inspection: black paste |
150℃ -30 minutes |
1kg |
Heat cycle resistance |
Exterior paint for hybrid IC |