Perurethane Epoxy resin for prototype model NM-350A/NM-350BHandling Company
Pelnox| Image | Part Number | Price (excluding tax) | Comparison of properties depending on curing conditions Impact strength | Comparison of properties by curing conditions Deflection temperature under load | Comparison of properties by curing conditions Hardness | Comparison of properties depending on curing conditions Flexural modulus | Comparison of properties by curing conditions Bending strength | Properties after curing: Impact strength | Characteristics after curing Deflection temperature under load | Properties after curing Hardness | Characteristics after curing Appearance of cured product | Properties after curing Flexural modulus | Properties after curing: Bending strength | Properties before curing Mixing ratio | Properties before curing Viscosity | Properties before curing Specific gravity | Properties before curing Maximum exothermic temperature | Properties before curing Appearance | Properties before curing Pot life | Properties before curing Initial mixing viscosity | Condition before curing Gel time | Purpose | Standard curing conditions | Packing form | Function | Category |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
|
|
NM-350A |
Available upon quote |
JIS K-7110 Izos with V notch, 25℃/16h + 60℃/4h: 3kJ/m2・25℃/16h + 80℃/4h: 6kJ/m2 |
JIS K-7191 Load 1.8MPa, 25℃/16h + 60℃/4h: 71℃・25℃/16h + 80℃/4h: 90℃ |
JIS K-7215 25℃, 25℃/16h + 60℃/4h: 86 (Shore D) ・25℃/16h + 80℃/4h: 86 (Shore D) |
JIS K-7171, 25℃/16h + 60℃/4h: 2,500MPa・25℃/16h + 80℃/4h: 2,200MPa |
JIS K-7171, 25℃/16h + 60℃/4h: 103MPa・25℃/16h + 80℃/4h: 101MPa |
JIS K-7110 Izos with V-notch: 11kJ/m2 |
JIS K-7191 Load 1.8MPa: 120℃ |
JIS K-7215 25℃：86 (shore D) |
Visual inspection: yellow transparent |
JIS K-7171: 2,400MPa |
JIS K-7171: 114MPa |
・Weight ratio: 100/33 |
25℃: 2,000mPa・s |
25℃: 1.17 |
・25℃, 100g: -℃ |
Visual observation: pale yellow liquid |
・25℃, 100g: -min |
25℃: 640mPa・s |
24℃, 100g: 157min |
Prototype model |
25℃/16hrs + 60℃/2hrs + 120℃/10hrs |
17kg |
Heat resistance Long pot life |
Epoxy resin for prototype model |