Perurethane Epoxy resin for prototype model NM-102A/NM-110B (Long pot life type)Handling Company
Pelnox| Image | Part Number | Price (excluding tax) | Properties after curing: Impact strength | Characteristics after curing Deflection temperature under load | Characteristics after curing Linear expansion coefficient | Properties after curing Hardness | Characteristics after curing Specific gravity of cured product | Characteristics after curing Appearance of cured product | Characteristics after curing Curing conditions | Properties after curing Flexural modulus | Properties after curing: Bending strength | Properties after curing: Tensile strength | Characteristics after curing Shrinkage rate | Properties after curing: Elongation rate | Characteristics after curing Glass transition temperature | Properties before curing Mixing ratio | Properties before curing Viscosity | Properties before curing Mixed viscosity | Properties before curing Specific gravity | Properties before curing Appearance | Properties before curing Pot life | Purpose | Standard curing conditions | Packing form | Function | Category |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
|
|
NM-102A (Long pot life type) |
Available upon quote |
JIS K-7110 Izod V-notch: 10kJ/m2 |
JIS K-7207 Load 1.8MPa: 55℃ |
TMA method: 8.1×10^-5/℃ |
ASTM D-2240 25℃: 82 (shore D) |
JIS K-7112: 1.15 |
Visual inspection: colorless and transparent |
60℃×3 hours |
JIS K-7171: 2,650MPa |
JIS K-7171: 90MPa |
JIS K-7113: -MPa |
T=4 Internal standard: -% |
JIS K-7113:-% |
TMA method: 75℃ |
・Weight ratio: 100/45 |
25℃: 13,500mPa・s |
25℃: 1,100mPa・s |
25℃: 1.17 |
Visual observation: pale blue transparent liquid |
25℃：3 |
Prototype model |
60℃-3hour |
5kg |
Heat resistance High transparency Long pot life |
Epoxy resin for prototype model |