Perurethane Epoxy resin for prototype model NM-102A/NM-102BHandling Company
Pelnox| Image | Part Number | Price (excluding tax) | Properties after curing: Impact strength | Characteristics after curing Deflection temperature under load | Characteristics after curing Linear expansion coefficient | Properties after curing Hardness | Characteristics after curing Appearance of cured product | Characteristics after curing Curing conditions | Characteristics after curing Thermal conductivity | Properties after curing Flexural modulus | Properties after curing: Bending strength | Properties after curing: Tensile strength | Characteristics after curing Shrinkage rate | Properties after curing: Elongation rate | Properties before curing Mixing ratio | Properties before curing Viscosity | Properties before curing Specific gravity | Properties before curing Appearance | Properties before curing Pot life | Condition before curing Gel time | Purpose | Standard curing conditions | Packing form | Function | Category |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
|
|
NM-102A |
Available upon quote |
JIS K-7110 Izod with V-notch: 5kJ/m2 |
JIS K-7191 Load 1.8MPa: 117℃ |
TMA method: 6.9 x 10^-5/℃ |
ASTM D-2240 25℃: 84 (Shore D) |
Visual inspection: colorless and transparent |
70℃ -2 hours |
Hot wire method: 0.21W/mK |
JIS K-7171: 2,800MPa |
JIS K-7171: 122MPa |
JIS K-7113: 82MPa |
T=4 Internal standard: 0.23% |
JIS K-7113: 5% |
・Weight ratio: 100/30 |
25℃: 13,500mPa・s |
25℃: 1.17 |
Visual observation: pale blue transparent liquid |
25℃: 90 minutes |
70℃: 25 minutes |
Prototype model |
70℃-2 hours |
5kg |
Heat resistance High transparency |
Epoxy resin for prototype model |