Perurethane Urethane resin for prototype model MU-858A/MU-858BHandling Company
PelnoxCategories
| Image | Part Number | Price (excluding tax) | Properties after curing: Flame retardant | Properties after curing: Impact strength | Characteristics after curing Deflection temperature under load | Properties after curing Hardness | Characteristics after curing Specific gravity of cured product | Characteristics after curing Appearance of cured product | Characteristics after curing Curing conditions | Properties after curing Flexural modulus | Properties after curing: Bending strength | Properties after curing: Tensile strength | Characteristics after curing Shrinkage rate | Properties after curing: Elongation rate | Properties before curing Mixing ratio | Properties before curing Viscosity | Properties before curing Specific gravity | Properties before curing Appearance | Properties before curing Pot life | Purpose | Standard curing conditions | Packing form | Function | Category |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
|
|
MU-858A |
Available upon quote |
UL94 File Number E62027：V-0 (3.0mm) |
JIS K-7110 Izod V-notch: 10kJ/m2 |
・JIS K-7191 Load 1.8MPa: 85℃ |
JIS K-7215 25℃：80 (shore D) |
JIS K-7112 25℃: 1.3 |
Visual inspection: white, black |
60℃×60 minutes |
JIS K-7171: 2,000MPa |
JIS K-7171: 90MPa |
JIS K-7161: 62MPa |
T=4 Internal standard: 0.3% |
JIS K-7161: 13% |
Weight ratio: 100/170 |
25℃: 850mPa・s |
25℃: 1.28 |
Visual inspection: colorless and transparent (uncolored), black |
25℃, 100g: 5min |
Prototype model |
60℃-90min or 70℃-60min |
1Kg |
Flame retardant (UL-94, V-0 certified) |
Urethane resin for prototype model |