Perurethane Urethane resin for prototype model MU-854A/MU-852BHandling Company
PelnoxCategories
| Image | Part Number | Price (excluding tax) | Properties after curing: Impact strength | Characteristics after curing Deflection temperature under load | Characteristics after curing Linear expansion coefficient | Properties after curing Hardness | Characteristics after curing Specific gravity of cured product | Characteristics after curing Appearance of cured product | Properties after curing Flexural modulus | Properties after curing: Bending strength | Properties after curing Tensile modulus | Properties after curing: Tensile strength | Characteristics after curing Shrinkage rate | Properties after curing: Elongation rate | Properties before curing Mixing ratio | Properties before curing Viscosity | Properties before curing Specific gravity | Properties before curing Appearance | Properties before curing Pot life | Purpose | Standard curing conditions | Packing form | Function | Category |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
|
|
MU-854A |
Available upon quote |
JIS K-7110 Izod V-notch: 17kJ/m2 |
・JIS K-7191 Load 1.8MPa: 100℃ |
TMA method: 8.5×10^-5/℃ |
JIS K-7215 25℃：82 (shore D) |
JIS K-7112 25℃: 1.23 |
Visual inspection: white, black, cream |
JIS K-7171: 2,050MPa |
JIS K-7171: 89MPa |
JIS K-7162: 2,000MPa |
JIS K-7162: 58MPa |
T=4：0.3% |
JIS K-7162: 15% |
・Weight ratio: 100/200 |
25℃: 850mPa・s |
25℃: 1.11 |
Visual inspection: colorless translucent, black, cream |
・25℃, 100g: 5min |
Prototype model |
60℃-1hour or 70℃-30min |
1Kg |
Impact resistance |
Urethane resin for prototype model |