Perurethane Urethane resin for prototype model MU-851A/MU-852BHandling Company
PelnoxCategories
Image | Part Number | Price (excluding tax) | Properties after curing: Impact strength | Characteristics after curing Deflection temperature under load | Characteristics after curing Linear expansion coefficient | Properties after curing Hardness | Characteristics after curing Specific gravity of cured product | Characteristics after curing Appearance of cured product | Characteristics after curing Curing conditions | Characteristics after curing Thermal conductivity | Properties after curing Flexural modulus | Properties after curing: Bending strength | Properties after curing Tensile modulus | Properties after curing: Tensile strength | Characteristics after curing Shrinkage rate | Properties after curing: Elongation rate | Characteristics after curing Glass transition point | Properties before curing Mixing ratio | Properties before curing Viscosity | Properties before curing Specific gravity | Properties before curing Appearance | Properties before curing Pot life | Purpose | Standard curing conditions | Packing form | Function | Category |
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
![]() |
MU-851A |
Available upon quote |
JIS K-7110 Izod V with notch: 16kJ/m2 |
JIS K-7191 Load 1.8MPa: 93℃ |
TMA method: 8.8 x 10^-5/℃ |
JIS K-7215 25℃:82 (Shore D) |
JIS K-7112 25℃: 1.22 |
Visual inspection: white, cream, black |
70℃ -45 minutes |
0.23W/mK |
JIS K-7171: 2,200MPa |
JIS K-7171: 93MPa |
JIS K-7161: 2,140MPa |
JIS K-7161: 64MPa |
T=4:0.3% |
JIS K-7161: 17% |
TMA method: 91 |
・Weight ratio: 100/200 |
25℃: 750mPa・s |
25℃: 1.12 |
Visual: colorless, cream, black |
25℃, 500g: 5 minutes |
Prototype model |
・Liquid temperature: 30℃~40℃ |
1kg |
Impact resistance |
Urethane resin for prototype model |