Perurethane Electrical urethane resin MU-209A/MU-209BHandling Company
PelnoxCategories
| Image | Part Number | Price (excluding tax) | Characteristics after curing Dielectric constant | Characteristics after curing Dielectric loss tangent | Properties after curing Flame resistance | Characteristics after curing Linear expansion coefficient | Properties after curing Hardness | Characteristics after curing Thermal conductivity | Properties after curing: Tensile strength | Characteristics after curing Water absorption rate | Characteristics after curing Volume resistivity | Properties after curing: Elongation rate | Properties after curing Young's modulus | Characteristics after curing Glass transition temperature | Properties before curing Mixing ratio | Properties before curing Viscosity | Properties before curing Initial mixing viscosity | Properties before curing Initial mixing specific gravity | Properties before curing Specific gravity | Properties before curing Appearance | Properties before curing Pot life | Condition before curing Tack free | Condition before curing Gel time | Purpose | Standard curing conditions | Packing form | Function | Category |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
|
|
MU-209A |
Available upon quote |
JIS K 6911 1kHz 100kHz 1MHz: 6.4 4.1 3.8 |
JIS K 6911 1kHz 100kHz 1MHz: 12.3% 11.0% 7.1% |
UL-94 1/4 inch: V-0 equivalent |
Tg or higher: 17×10^-5/℃ |
JIS K 7215 25℃：65 (shore A) |
300g: 0.48W/m・K |
JIS K 7312 25℃ No. 2 dumbbell: 3.2MPa |
JIS K 6911 25℃ 24hrs: 2.31wt% |
JIS K 6911 25℃: 3.3×10^13 (Ω・cm) |
JIS K 7312 25℃ No. 2 dumbbell: 100% |
JIS K 7312 25℃ No. 2 dumbbell: 2.1MPa |
TMA method: -25℃ |
Weight ratio: 100/30 |
25℃: 12,000mPa・s |
25℃: 2,300mPa・s |
25℃: 1.45 |
25℃: 1.54 |
Visual inspection: black liquid |
Time to 25℃, 10Pa・s: 15min |
・60℃：20min |
60℃：20min |
Automotive electrical components circuit board |
60℃-2hour or 25℃-36hour |
20Kg |
Flexible Low Stress Impact Resistant Shock Absorption Stress Relief |
Urethane resin for electricity |