Pelnox <Epoxy sealing resin for electronics> UV curing resin AT17-SHandling Company
PelnoxCategories
| Image | Part Number | Price (excluding tax) | Characteristics after curing Moisture permeability | Properties after curing Dielectric breakdown strength | Characteristics after curing Insulation resistance | Properties after curing Tensile shear adhesive strength | Characteristics after curing Water absorption rate | Characteristics after curing Glass transition temperature | Properties before curing Average viscosity | Properties before curing Appearance | Purpose | Packing form | Recommended curing conditions | Function | Category |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
|
|
AT17-S |
Available upon quote |
JIS Z 0208, 200μm thickness: 52 (g/m2*24h) |
JIS C 2110-1: 40kV/mm |
60℃ 95%RH, 16V, 1,000h: ≧1.0×10^9Ω |
25℃, base material PET-PET: ≧7MPa |
JIS K 6911: 0.3% |
DSC method: 6℃ |
TVE-25H Corn plate 3°-R14 25℃: 34,000mPa・s |
Visual observation: pale yellowish white liquid |
Automotive electrical components Sensors, relays General modules |
1kg |
UV irradiation 1,600mJ/cm2 (approximately 1mm coating thickness, high pressure mercury lamp 365nm) |
One-component, flexible, low stress, low temperature curing, environmentally friendly, fast curing, UV curing |
UV curing resin |