Pelnox <Epoxy sealing resin for electronics> High voltage component insulation material ME-280/HV-140Handling Company
Pelnox| Image | Part Number | Price (excluding tax) | Characteristics after curing Linear expansion coefficient | Properties after curing Hardness | Characteristics after curing Thermal conductivity | Properties after curing Flexural modulus | Properties after curing: Bending strength | Properties after curing Tensile modulus | Properties after curing: Tensile strength | Characteristics after curing Water absorption rate | Characteristics after curing Volume resistivity | Characteristics after curing Glass transition temperature | Properties before curing Mixing ratio | Properties before curing Viscosity | Properties before curing Specific gravity | Properties before curing Appearance | Properties before curing Initial mixing viscosity | Condition before curing Gel time | Purpose | Standard curing conditions | Packing form | Function | Category |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
|
|
ME-280 |
Available upon quote |
・Tg or below: 2.2 (10^-5/℃) |
JIS K-7215 25℃: 93 Shore D |
JIS K-7191-3: 178℃ |
JIS K-6911: 8,200MPa |
JIS K-6911: 49MPa |
JIS K-7161: 4,400MPa |
JIS K-7161: 29MPa |
・JIS K 6911 Boiling 2 hours: 0.12wt% |
・JIS K 6911 25℃：6.6 x 10^15 (Ω-cm) |
TMA method: 173℃ |
Weight ratio: 100/100 |
25℃: 77,000mPa・s |
25℃: 1.82 |
Visual inspection: brown liquid |
25℃: 34,000MPa・s |
100℃ 40g: 30 minutes |
High pressure parts resin insulator |
100℃-1 hour +150℃-3 hours |
20kg |
Weather resistance Flame retardant (UL-94, V-0 certified) High Tg |
High voltage component insulation material |