Pelnox <Epoxy sealing resin for electronics> Resin for automotive electrical components and various sensors ME-352/HV-132 (low viscosity type)Handling Company
Pelnox| Image | Part Number | Price (excluding tax) | Properties after curing: Flame retardant | Characteristics after curing Linear expansion coefficient | Characteristics after curing Dielectric breakdown voltage | Properties after curing Hardness | Characteristics after curing Heat distortion temperature | Properties after curing Flexural modulus | Properties after curing: Bending strength | Characteristics after curing Water absorption rate | Characteristics after curing Volume resistivity | Characteristics after curing Glass transition temperature | Properties before curing Mixing ratio | Properties before curing Viscosity | Properties before curing Specific gravity | Properties before curing Appearance | Properties before curing Initial mixing viscosity | Condition before curing Gel time | Purpose | Standard curing conditions | Packing form | Function | Category |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
|
|
ME-352 (low viscosity type) |
Available upon quote |
UL-94: V-0 certified |
・Tg or below: 6 (10^-5/℃) |
JIS K-6911: 16kV/mm |
JIS K-7215 25℃: 90 Shore D |
JIS K-7191-3: 98℃ |
JIS K-6911: 4,300MPa |
JIS K-6911: 84MPa |
JIS K 6911 Boiling 1 hour: 0.28wt% |
JIS K 6911 25℃: 8.0 x 10^16 (Ω-cm) |
TMA method: 92℃ |
Weight ratio: 100/39 |
25℃: 24,000mPa・s |
25℃: 1.58 |
Visual observation: black viscous liquid |
25℃: 1,700mPa・s |
100℃: 27 minutes |
Film capacitor general module |
100℃-1 hour |
5kg |
Flame retardant (UL-94, V-0 certified) |
Resin for automotive electrical components and various sensors |