Product
Magnetic and oxide crystalsHandling Company
Tours Co., Ltd.Items marked with have different values depending on the model number.
Click on the part number for more information about each product
Product Image | Part Number | Price (excluding tax) | AR coating | BiCrystal | Crystal direction | Crystal lattice | Crystal structure | Dealing loss (300k) | Direction | Expenditure rate | Heat expansion coefficient | Indirect dielectric | Lattice constant | Loss of propagation | Melting point | Morse hardness | Nurturing direction | Open -minded | Parallelity | Permeability | Permeation range | Phase speed | Ratio of lighting | Ratio resistance | Refractive index | Surface polishing accuracy | Temperature coefficient | Thermal conductivity | Training method | Vertical degree | Wave surface distortion | Zebeck coefficient | color | composition | density | purity | size | specific heat |
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
Mgal2o4 |
Available upon quote | - | - | - | - | Cube: a = 8.085å | - | <100>, <110>, <111> | - | 7.45x10⁻⁶/℃ | - | - | 6.5db/MS | 2,100 ° C | 8 | - | - | - | Approximately 85%or more | 0.2 ~ 500nm | 6,500m/s at <100> | - | - | - | RA <5å | - | 14.0W/ (M.K) (25 ℃) | CZ method | - | - | - | - | - | 3.64g/cm³ | - |
φ2 "x0.5mm φ1 "x0.5mm 40x20x2mm 20x20x0.5mm 10x10x0.5mm Other desired size |
- | |
MGO |
Available upon quote | - | - | - | a = 4.216å | cube | - | - | <9.5 | 12.8x10⁻⁶/℃ | - | - | - | 2,850 ° C | 5.5 | - | - | - |
> 90% (200-400Nm) > 98% (500-1,000nm) |
200 ~ 8,000nm | - | - | > 10¹⁷Ohm.cm | NC = 1.77197 ~ 1.72267 | - | - | - |
Chokural skiing (China) Ark Electric Furnace (Germany) Both (100) orientation |
- | - | - | - | - | 3.58g/cm³ |
99.95% (China) 99.99%or more (Germany) |
- | - | |
Laalo3 |
Available upon quote | - | - | - | - | Pseudo -based crystal (Perobskite), Akira Mikata | - | (100), (110), (111) | 13 ~ 25 (fluctuated by the manufacturer) | 1x10⁻⁵K⁻¹⁻¹ |
3x10⁻⁴ at 300k 6x10⁻⁵ at 77k, 10GHz (Tandel) (Electrical energy loss) |
(Akira Sanpo) A = 5.357å (x = 60 ° 6 ') (Perobskite) a = 3.863å (x = 90 ° 5 ') * If there is no specification, it is a perovskite. |
- | 2,080 ° C | 5.9 | -100 | - | - | - | - | - | - | - | n = 2.0 | - | - | - | - | - | - | - | Bright brown like whiskey | - | 6.52g/cm³ | - | - | - | |
Zno |
Available upon quote | - | - |
C side (0001) A side (11-20) M side (10-10) |
- | Rokuku crystal Urtz structure | - | - | - |
6.5x10⁻⁶/℃: A axis parallel 3.7x10⁻⁶/℃: C axis parallel |
- | A = 3.252å C = 5.313å | - | 1,975 ℃ | Four | - | - | - | - | 400 ~ 600nm@> 50%/T2mm | - | - | - | - | - | - | 0.006cal/cm/k | - | - | - | 1200UV/K at 300 ℃ | - | - | 5.7g/cm³ | - | - | - | |
SRTIO3 |
Available upon quote | - |
(100), 12 °, 24 °, 36 ° You can also do another side direction and angle. |
- | a = 3.905å | Cube | 5x10⁻⁴ | (100), (110), (111), (305) | 300 | - | - | - | - | 2,080 ° C | 6 ~ 6.5 | - | -100 | - | - | 395 ~ 6,000um | - | - | - | - | - | - | 11.2W/m ・ K | Bernouy (flame melting method) | - | - | - | Transparent (rarely may be slightly yellow due to flame melting.) | - | 5.175g/cm³ | - | - | 0.544J/G/K (300k) | |
Ggg |
Available upon quote | - | - | - | - | Cube, M3 | - | - | 30 | - | Ca.3*10⁻⁴ (10GHz) | a = 12.376å (z = 8) | - | 1,730 ° C | 6 ~ 7 | - | - | - | - | 0.3 ~ 7.0mm | - | - | - | ND = 1.9708 at 577nm | - | - | - | CZ method | - | - | - | - | - | 7.09g/cm³ | - | - | - | |
Tgg |
Available upon quote | <0.2% | - | (111) Within 5 ° | - | - | - | - | - | - | - | a = 12.355å | - | 1,725 ℃ | 8 | - | - | Within 1 minute | - | - | - | > 30db | - | 1.954 at 1064nm | - | 9.4x10⁻⁶ ℃ ⁻¹ | - | Cz | <1 ° | > 1/8 633nm | - | - | - | 7.13g/cm³ | - | - | - | |
Lsat |
Available upon quote | - | - | - | - | Cubic crystal/Cube -containing pelob scite structure | - | (100), (110), (111) | twenty two | 10x10⁻⁶ ℃ | - |
A = 7.737å A/2 = 3.868å |
- | 1,840 ° C | 6.5 | - | - | - | - | - | - | - | - | - | - | - | - | Chokur ski | - | - | - | Pale yellow or transparent | (La0.3sr0.7) (AL0.65ta0.35) O3 | 6.74g/cm³ | - | - | 5.1W | |
Ysz |
Available upon quote | - | - | - | - | cube | - | - | 27 (1MHz) | 10.3x10⁻⁶/℃ | - | a = b = c = 5.125å | - | 2,500 ° C to 2,780 ° C | 8 | - | - | - | - | 400 ~ 6,500Nm | - | - | - | ND = 2.15 | - | - | - | Skarmelting, flux | - | - | - | - | - | 5.8g/cm³ | 99.99% | - | - | |
SNO2 |
Available upon quote | - | - | - | a = 4.737å | Rutile type regular crystal | - | (100), (001), (110), (111) | - | - | - | - | - | 1,630 ° C | 7 | - | - | - | - | - | - | - | - | 2.006 | - | - | - | - | - | - | - | - | - | 6.95g/cm³ | - |
Square: 1x1 to 10x10mm Round: From φ1 to φ10mm It can be processed at each desired size. |
52.6j/mol.k |