SPR5200BK (Fine Peek BLACK) is a cutting material for cutting and molding a PEEK fine processing grade (insulation / black). ■ Features of SPR5200BK ・ Share method: Ejecting injection formation ・ Wearing resistance ・ Easy to remove after processing and can be finely processed after processing. ・ Low cost: Realizes the lower cost of mother material by injection molding ・ Color: By making it black, it is possible to support image processing handlers
You can search for other models from each index. The displayed value is the value of the currently selected part number.
Bending elasticity rate
Bending strength
Glass transfer temperature (TG)
Hammer material size shape
Homber size thickness (mm)
Line expansion rate
Maternal material size angle (mm)
Mother material size MOQ/SPQ
Notch with a notch with a shock strength
Surface resistance value
Tensile strength
Tenstration destroyed strain
Water absorption rate
Part Number
SPR5200BKHandling Company
PBI Advanced Materials Co., Ltd.Items marked with have different values depending on the model number.
Product Image | Price (excluding tax) | Bending elasticity rate | Bending strength | Glass transfer temperature (TG) | Hammer material size shape | Homber size thickness (mm) | Line expansion rate | Maternal material size angle (mm) | Mother material size MOQ/SPQ | Notch with a notch with a shock strength | Surface resistance value | Tensile strength | Tenstration destroyed strain | Water absorption rate |
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
Available upon quote | 8.0GPa (Condition: 23 ° C, Standard: ISO 178) | 200MPa (Condition: 23 ° C, Standard: ISO 178) | ~ 140 ° C (standard: DSC) | Plate | 4,6,10 | 29ppm/℃ (Condition: <tg, Standard: JIS K7197) | 204 x 305 | 1/1 | 4.4kj/m^2 (Condition: 23 ° C, Standard: ISO 179) | > 10^13Ω (Condition: 23 ° C, Standard: ANSI/ESD STM11.13) | 110MPa (Condition: 23 ° C, Standard: ISO 527) | 2.5% (Condition: 23 ° C, Standard: ISO 527) | 0.04% (Condition: 23 ° C, 24hr, Standard: ISO 62) |
PBI Advanced Materials Co., Ltd.